| Product
Name |
Description |
Features /
benefits |
Typical
Applications |
Technical Information
|
Dosage / coverage |
Packing
Available |
| Silicone
Sealant WX |
Acetic cure
silicone sealant for windows |
● Ready to
use, solvent free
● Non sagging
● Flexible at low & high temperature
● Fast rate room temperature cure
● Fast rate room temperature cure
● No primer is required when sealing joints in glass,
ceramics and vitreous surfaces
● Forms tough, durable and elastic seal
● Low shrinkable, good UV resistance & insulation
properties
Shelf Life : 1 year |
Ideal to
seal gap between glass and aluminum in lieu of rubber
beading, painted surfaces, ceramics, fiber glass, non
oily woods, etc. |
● Curing
type : Acetoxy
● Colour : Black
● Density : Approx : 1.04 gm/cc
● Skin formation time : Approx 5 minutes at 30
ºC
● Curing Time : Approx 24 hrs. for 2 mm thickness at 30
ºC
●Movement accommodation : Approx 15 %
● Tensile strength : Approx 0.61 N/mm
● Elongation at break : Approx : 260 % |
35-40 RFT for 280 ml
cartridge for 5 mm x 5 mm joint |
280 ml plastic
cartridge with separate nozzle available in black colour |
|
Sillicone Sealant GPS |
Acetic Cure
silicone sealant for windows |
● Ready to
use, solvent free
● Non sagging
● Flexible at low and high temperatures.
● Fast rate room temperature cure
● No primer is required when sealing joints in glass,
ceramics and vitreous surfaces
● Forms tough, durable and elastic seal
● Low shrinkage, good UV resistance & insulation
properties |
Ideal to
seal gap between glass and aluminium non oily wood,
sealing of aluninium / glass window frame joints, fixing
glass into aluminium frames in lieu of rubber beading |
● Curing
type : Acetoxy
● Colour : Translucent
● Density : Approx : 0.93 gm/cc
● Skin formation time : Approx 10 minutes at 30
ºC
● Curing Time : Approx 24 hrs. for 2 mm thickness at 30
ºC
●Movement accommodation : Approx 15 %
● Elongation : Approx : 380 % |
??? |
250 ml plastic
cartridge with saperate nozzle |
|
Pidiseal PS 41 G
(Gun Grade)
42P
(Pouring Grade) Specification:
complies with
BS 4254 - 1983
|
Two Part
Polysulphide Sealant |
● Ambient
temperature curing
● Forms a permanent tough elastic rubber
, seal
● Excellent adhesion to a wide range of
building material
● Accommodates continuous and
pronounced cyclic movements
● Very low shrinkage
● Good slump resistance (To be deleted)
● Resistant to sunlight (UV rays)
● Resistant to bio-degradation
● Resistant to occasional spillage of dilute acids,
alkalis, petrol, aviation fuels, diesel, kerosene,
lubricating oils etc.
● Non-toxic
Shelf Life : 1 Year
|
● Sealing
of moving and
construction joints as
well as joints between
different construction
materials in high rise buildings, concrete highways,
bridges,
water retaining.
structures, basements,
subways, culverts, .
airfields, etc.
● Internal and external wall claddings
● Vertical joints in retaining
walls
● Vehicular and pedestrian App
traffic pavements of concrete
|
● Brass :
Cross linking Liquid
Polysulphide Polymer
● Colour:
Part. A Off White,
Part. B Black,
Mixed material - grey in colour
● Mix ratio (Base/Accelerator): 92:8 (Wt by Weight)
● Density (Mix) :1.58 ± 0.03
kg/
Itr
● Pot Ute : More than 2 hrs at
3O"C
● Complete Cure Rate:
Approx. 8 weeks at 5°C
Approx. 4 weeks at 15°C
Approx.2 weeks at 25°C
Approx. 8 days at 35°C
● Shore A hardness:
-22 (after complete curing)
● Movement Accommodation:
25% for butt joints and 50 %
for lap joints
● Joint size : For 5 to 50 mm
depth to width ratio should
e 1 : 2 (min).
● For joints with skew
Movements, the ratio can as
upto 1 : 1
|
2 RMT / kg for a 25 mm X 12 mm joint |
1kg, 4 kg, 6.5 kg |
Pidiseal PS 43
Specifications meets the requirements of BS 5212 -
1990 N, F & FB type Federal Spec
SS -S- 200 E - 1984 |
Fuel &
Flame
Resistant
Specification: Sealant for Highways, expressways,
runways & pavements |
● Cold applied, no
pre-heating is required .
● Pouring grade ·
● Fuel resistance
● Tough, elastomeric in nature
● UV resistance and highly durable in I
outdoor application
● Accommodates continuous and
pronounced cyclic movements .
● No maintenance required during service
life ,.
Shelf Life : 1 Year |
● Concrete
highways
● Garages
● Airport runways
● Bridges
● Aircraft fueling areas
● Subways
● Parking and cargo areas
● High rise buildings
|
● Appearance : Two part
(both parts are black in colour)
● Mix ratio: Part A : Part B = 92 : 8 (by weight) ,
● Specific gravity: 1.55 ±
0.02
Solid Content: 100% ~
● Pot life : 2 to 5 hour at 300C
(For 6.5 kg mix)
● Shrinkage : less than 1 %
● Movement accommodation -
factor: 25% for butt joints |
2 RMT / kg for a 25 mm X 12 mm joint |
6.5 Kg Composite
Pack |